TYPICAL PROPERTIES OF UNCURED MATERIAL
Viscosity, HAAKE RV-20 Rotoviscometer, mPa·s (cP):
Cone 1º @ Shear rate 22 s
-1 9,000
Work Life @ 25°C, hours 8 to 16
Shelf Life @ -40°C (from date of manufacture), days 365
TYPICAL CURING PERFORMANCE
Cure Schedule
30 minutes @ 150°C
Suggested temperature cures are from 150 to 350ºC. For
applications requiring higher electrical conductivity, a cure cycle of 15
minutes @ 300ºC is recommended. Product properties will not be
reduced by subsequent post die attach thermal exposure, i.e.,
wirebond, and/or lid seal up to 370ºC.
TYPICAL PROPERTIES OF CURED MATERIAL
Physical Properties
Coefficient of Thermal Expansion, :
Below Tg, ppm/°C 33
Glass Transition Temperature (Tg) by TMA, °C 240
Bulk Thermal Conductivity, W/(m-K):
@ 90°C 1.1
@ 165°C 1.0
Tensile Modulus, DMTA :
Cured 30 minutes @ 300ºC N/mm² 10,000
(psi) (1,450,377)
Extractable Ionic Content, @ 100°C:
Chloride (Cl-) <10
Sodium (Na+) <15
Potassium (K+) <15
Decomposition (in N2):
TGA analysis @ 10ºC/ minute ramp from 25 to 400
ºC
@ 340ºC, % 0.2
@ 400ºC, % 0.3
Electrical Properties
Sample cured 30 minutes @ 300ºC
Volume Resistivity, ohm-cm ≤0.01
TYPICAL PERFORMANCE OF CURED MATERIAL
Die Shear Strength:
2 X 2 mm Si die, kg-f,
cured 20 minutes @ 150ºC
Substrate DSS
Ag/Cu LF ≥5
Tensile Strength :
cured 30 minutes @ 300ºC, MPa
After Cure After 1000 TC'C"
>17 >17
Radius of Curvature:
Si die on Alumina, meters
cured 30 minutes @ 300ºC
Chip Size: ROC
15 x 15 mm > 5
汉高乐泰导电胶,杨浦厚膜汉高ABLESTIKJM7000导电胶
面议
产品名：汉高ABLESTIKJM7000导电胶,JM7000导电胶,汉高导电胶,乐泰导电胶
ablestik84-1A导电胶
面议
产品名：导电胶,耐高温导电胶,84-1A导电胶,84-1LMI导电胶
高导热导电胶军工导电胶导电胶双85导电胶耐高温导电胶
面议
产品名：高导热导电胶,导热导电胶,导电胶,纳米银胶
单组份常温贮存导电胶军工导电胶双85导电胶可代替H20E
面议
产品名：导电胶,烧结银,导电银浆,导电银胶
厚膜浆料杜邦浆料代替品军工浆料钯银浆料玻璃浆料
面议
产品名：厚膜浆料,钯银浆料,玻璃浆料,钯金浆料
浙江汉高乐泰2850FT环氧灌封胶颜色
面议
产品名：乐泰2850FT环氧灌封胶,2850ft灌封胶,2850灌封胶,环氧灌封胶2850FT
香港进口汉高乐泰144A耐高温环氧胶传感器,乐泰144A
面议
产品名：乐泰144A耐高温环氧胶,乐泰144A单组份环氧胶,乐泰144A,耐高温环氧胶
澳门TSV小型晶圆喷镀台MEMS
面议
产品名：TSV小型晶圆喷镀台,晶圆电镀机,晶圆喷镀机,晶圆电镀台