吸湿发热整理剂 HOLPOSON® HOT



HOLPOSON® HOT 适合用于棉，粘胶，涤纶，晴纶等各种纤维的后整理。其作用原理 HOLPOSON® HOT 是处理在面料上，使面料周围的水蒸气或者汗蒸汽凝聚成水珠或者汗珠所产出的凝聚热，让人体感受到暖感，从而达到蓄热保暖的功能。

一、物化性能

组成 特殊聚丙烯酸等

外观 微黄色透明弱粘液体

离子性 弱阳离子

溶解度 溶解于水

PH值 5～6



二、使用方法

用量：因被处理物的种类而异，一般为6.0~10.0%（o.w.f.）

1、浸轧法

用量： HOLPOSON® HOT 80~130g/l

处理方法：二浸二轧，带液率在80%左右，120℃以上烘干定型

2、浸渍法（适用棉、粘胶）

用量：6-10%（o.w.f.）

均匀化料整理液 浸渍（20分钟） 脱水（带液量50%左右） 烘干（80℃） 定型（120度，1-2分钟）

3、熔丝法

根据实际，结合技术建议用量配制材料



注意事项

产品使用前请确认面料是否处理疏水柔软剂,建议添加亲水性柔软剂，配制好的工作液请于当日内使用



贮 存

室内存放，避免高温、严寒。

Hydroscopic and Heat Releasing Finishing Agent

HOLPOSON® HOT

HOT is suitable for finishing cotton, viscose, polyester, acrylic and other fibers. Its working principle is as follows: The product treated on the fabric make the water vapor or sweat vapor around the fabric condense into water drops. And the condensation heat produced makes the human body feel warm, so as to achieve the function of heat storage and warmth preservation.


Physical & chemical properties:

Composition: Special polyacrylic acid, etc.

Appearance: Yellowish transparent weak viscous liquid

Ionicity: Weak cationic

Solubility: Soluble in water

pH: 5-6



Usage:

Dosage: Depends on different types of materials to be treated. Generally 6.0-10.0% (o.w.f.)

1. Padding method

Dosage: HOT 80-130g/L

Treatment method: Dip and roll twice, with liquid rate of about 80%, drying and heat setting above 120 ℃

2. Impregnation method (applicable to cotton and viscose)

Dosage: 6-10% (o.w.f.)

Dissolv evenly to prepare the solution → impregnation (20 minutes) → dehydration (about 50% of liquid content) → drying (80 ℃) → heat setting (120 ℃, 1-2 minutes)

3. Melt spinning method

Prepare the solution according to the actual situation and technical suggestions.



Attentions:

Before using the product, please confirm whether the fabric is treated with hydrophobic softener. It is recommended to add hydrophilic softener. The prepared working solution should be used within the same day.

Storage:

1. Store indoor

2. Avoid overheat and severe cold